WANG Shuai, ZENG Jiang, ZHANG Zhimeng, SONG Jie, ZHANG Shuxin. Cause of Bursting of Choke Line in Oilfield Well Control Device[J]. Materials and Mechanical Engineering, 2023, 47(3): 98-102. DOI: DOI: 10.11973/jxgccl202303017
Citation: WANG Shuai, ZENG Jiang, ZHANG Zhimeng, SONG Jie, ZHANG Shuxin. Cause of Bursting of Choke Line in Oilfield Well Control Device[J]. Materials and Mechanical Engineering, 2023, 47(3): 98-102. DOI: DOI: 10.11973/jxgccl202303017

Cause of Bursting of Choke Line in Oilfield Well Control Device

More Information
  • Received Date: January 15, 2022
  • Revised Date: February 05, 2023
  • The choke line of an oil well in an oilfield bursted during the sidetracking process. The reason for bursting of the choke line was analyzed by macromorphology observation, non-destructive testing, chemical composition analysis, mechanical performance testing and fracture morphology observation, as well as internal pressure resistance checking of the burst choke line. The results show that before being used this time, the external wall of the choke pipeline with axial penetration cracks was repaired by welding treatment. The thickness of the repairing weld was very small, and much less than pipeline wall thickness, resulting in the bursting failure during sidetracking because of insufficient bearing capacity of the pipeline. Meanwhile, the poor toughness and impact performance of the pipeline promoted the occurrence of brittle fracture.
  • [1]
    陈惠玲.节流管汇存在的问题及改进措施[J].天然气工业,1998,18(4):91-92.

    CHEN H L.Problems in throttle manifold and improvement measures[J].Natural Gas Industry,1998,18(4):91-92.
    [2]
    苗向阳,牛逵,阮姣姣,等.塔里木油田高压气井节流管汇刺漏问题研究[J].中国石油和化工标准与质量,2014,34(7):76.

    MIAO X Y,NIU K,RUAN J J,et al.Study on leakage of throttle manifold of high pressure gas well in Tarim oilfield[J].China Petroleum and Chemical Standard and Quality,2014,34(7):76.
    [3]
    付玉坤,王娟,张克亮.油气田钻井节流管汇系统的技术发展[J].石油和化工设备,2015,18(6):5-8.

    FU Y K,WANG J,ZHANG K L.Technical development of throttle manifold system for oil and gas field drilling[J].Petro & Chemical Equipment,2015,18(6):5-8.
    [4]
    邓时钊.节流压井管汇在井控技术中的应用[J].技术与市场,2018,25(12):93-94.

    DENG S Z.Application of choke and kill manifold in well control technology[J].Technology and Market,2018,25(12):93-94.
    [5]
    李荣光,张巍,赵振,等.高钢级管道环焊缝缺陷修复技术探讨[J].油气储运,2020,39(3):307-312.

    LI R G,ZHANG W,ZHAO Z,et al.Discussion on repair technology of girth weld defects of high-grade steel pipelines[J].Oil and Gas Storage and Transportation,2020,39(3):307-312.
    [6]
    胡桢睿.浅析天然气管道缺陷修复技术[J].内蒙古石油化工,2019,45(6):95-97.

    HU Z R.Analysis on the repair technology of natural gas pipeline defects[J].Inner Mongolia Petrochemical Industry,2019,45(6):95-97.
    [7]
    吕拴录,龚建文,卢强,等.提升短节外螺纹接头断裂原因分析[J].机械工程材料,2011,35(2):86-88.

    LV S L,GONG J W,LU Q,et al.Fracture cause analysis of lift sub external nipple[J].Materials for Mechanical Engineering,2011,35(2):86-88.
    [8]
    吕拴录,李元斌,冯春,等.某井油管接箍开裂原因分析[J].理化检验-物理分册,2014,50(2):149-154.

    LV S L,LI Y B,FENG C,et al.Causes analysis on cracking of tubing coupling in one well[J].Physical Testing and Chemical Analysis (Part A:Physical Testing),2014,50(2):149-154.
    [9]
    龙岩,李岩,马磊,等.西部某油田修复油管的断裂原因[J].腐蚀与防护,2018,39(5):359-364.

    LONG Y,LI Y,MA L,et al.The fracture reason of repaired tubing in a western oilfield[J].Corrosion & Protection,2018,39(5):359-364.
    [10]
    张春婉,张国正,史李镛,等.套管在静水压试验时发生爆裂的原因[J].机械工程材料,2012,36(3):97-100.

    ZHANG C W,ZHANG G Z,SHI L Y,et al.Cracking reason of casings during hydrostatic test[J].Materials for Mechanical Engineering,2012,36(3):97-100.
    [11]
    王艳阳,陈斌,后宗保,等.脱碳层深度测量方法比较[J].理化检验-物理分册,2020,56(5):23-26.

    WANG Y Y,CHEN B,HOU Z B,et al.Comparison of decarburization depth measurement methods[J].Physical Testing and Chemical Analysis (Part A:Physical Testing),2020,56(5):23-26.
    [12]
    陈连生,李跃,宋进英,等.55Mn冷轧带钢边裂的产生原因及冷轧控制措施[J].机械工程材料,2017,41(8):31-34.

    CHEN L S,LI Y,SONG J Y,et al.Reason for edge cracking of cold-rolled 55Mn strip steel and the cold-rolling control measures[J].Materials for Mechanical Engineering,2017,41(8):31-34.

Catalog

    Article views (2) PDF downloads (4) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return